WellubTM Waxes are Polyolefin Wax, Oxidized Polyethylene Wax and FT wax produced by Sundow Polymers Co.,LTD. The polyethylene wax is fully saturated homopolymers of ethylene, which has high degree of crystalline and linearity. PE wax has a high crystalline value and thus it has attributes like low solubility in solvents, higher hardness at elevated temperatures and oil thickening capability. Compared with PE Wax, the molecule structure of OPE Wax have some hydroxyl groups on them. So the intermiscibility with the polar resin will been improved a lot. It is better than PE wax when it is with the polar material.

CONTACT US PDF FORMAT
  • Introduction
  • Selection Guide
  • Application

n General introduction

Wax.jpgWaxes are widely used throughout the world for a range of applications, including packaging, coatings, cosmetics, foods, adhesives, inks, castings, crayons, chewing gum, polishes, candles, paints, plastic stabilizers, textile auxiliaries, masterbatch, foaming agent, plastic forming and other industries.

WellubTM Waxes are Polyolefin Wax, Oxidized Polyethylene Wax and FT wax produced by Sundow Polymers Co.,LTD.

The polyethylene wax is fully saturated homopolymers of ethylene, which has high degree of crystalline and linearity. PE wax has a high crystalline value and thus it has attributes like low solubility in solvents, higher hardness at elevated temperatures and oil thickening capability.  Compared with PE Wax, the molecule structure of OPE Wax have some hydroxyl groups on them. So the intermiscibility with the polar resin will been improved a lot. It is better than PE wax when it is with the polar material.

FT wax (Fischer-Tropsch wax) is manufactured with natural gas as a raw material. With its high melting point and low melting viscosity, this FT wax has hardness with excellent heat stability.

 

n  Characteristic of Wellub™ Waxes

²  Low toxicity, low reactivity

²  Low odor

² Extremely hard (Penetration 1 Max)

²  Excellent mold release/dispersion characteristics

² Excellent glossy effect

²  Sharp melting point/congealing point

² Excellent compatibility with resins


n  Selection Guide of Wellub™ Waxes

Type

Grade

Softening   Point

Viscosity,   CPS@140

Corresponding   Grade

Applications




     Fischer-tropsch  Wax

SF100

95-100

5-10

/


1. PVC stabilizer and PVCproducts

2. Hot melt adhesive.

3. Road marking painting.

4. Powder coating.

5. Filler masterbatch.

6. Asphalt modification.


SF105E

100-105

5-10

Shell SX105

Economic grade of SF105

SF105

100-105

5-10

Shell SX105

SF110

105-110

10-20

/

SF115

110-115

10-20

Sasol H1




       Polyethylene Wax

SP105

100-110

5-10

Sasol H1 or Shell SX105

1. PVC stabilizer and lubricant.

2. Lubricant and dispersant used in   rubber compound.

3. Dispersant and lubricant in the   color master-batch and filler master-batch.

4. Hot melt adhesives.

5. Hot melt road marking and   printing inks.

SP112

110-115

20-60

Sasol   H1 or Shell SX105, higher quality of SP105

SP119

110-115

400-600

BASF   Luwax-A


         




Oxidized Polyethylene Wax

SOP316

130-135

6000~9000

Honeywell   AC-316A

1. Dispersant for color master batch   processing.

2. Interior lubricant for PVC   products.

3. For water-based paint and ink,   the paint coating, polishes and textiles.

4. Improve the sewability and fabric   cuttingperformance in the textile.

5. For papermaking, printing, dyeing   and other industries after the emulsification.

SOP269

100-105

200-300

Honeywell   AC-629

Above is just part of our grades, if you want to know further information or more grades, please contact info@sundow.com.